Plastic Mould Steel
Thyssenkrupp 2316
Characteristic 2316
2316 steel are in the class of plastic mold and stainless steel which was developed from 2083 (AISI420)
By adding more composition of Chromium and Molybdinum, it can increase corrosive resistance
Moreover, it also comes with quenching and tempering as normal selling condition
Hardness is in range 300 HB (30 HRC), result in easy to machining without hardening againg
Also, help avoid changing in its dimension from hardening process
Suitable for plastic mold that require corrosive resistance during plastic making such as
PVC, Amino plastic and thermo plastic
Outstanding Properties 2316
• Higher corrosive resistance as compared to 2083 at its class
• Higher strength as compare to 2083
• Wear and corrosive resistance
• strength enough to stand for presssure from injection plastic mold
• Texturing properties in equivalent to 2311
• Machining ability is in moderate level
• Can do EDM well
• Risk free of damange from heat treatment process
• Homogeneity hardness throughout the whole thickness
• Hardening ability in high level
• Hardness after hardening process less than 2083
• Can do Passivation to enhance corrosive reisstance.
2316 Similar Properties/ Equivalent
|
Steel
Classification |
Standard
|
Assab
|
Bohler
|
Daido
|
Thyssen
|
Hitachi
|
|||
|
DIN
|
JIS
|
AISI
|
|||||||
|
Plastic
Mould Steel |
1.2316
|
SUS
420 J2 |
–
|
RaMaxS
|
M300
|
–
|
2316
|
HPM
38 |
|
|
1.2311
|
P20
|
718
|
W330
|
NAK 55
|
2311
|
||||
|
1.2312
|
P20+S
|
Holdax
|
M200
|
–
|
2312
|
||||
Availability
Roundbar: 10mm – 220mm
Flat: 10mm – 120mm
Chemical Composition 2316
| Type | C | Cr | Mn | Si | S | P | Ni/V | Mo |
| 2316 | 0.33-0.45 | 15.0-17.0 | 1.5 Max | 1.0 Max | 0.030 | 0.030 | 1.0 Max | 0.80-1.30 |
| SUS 420J2 | 0.26-0.40 | 12.00-14.00 | 1.00 | 1.00 | 0.030 | 0.040 | – | – |
Mechanical Properties
Hardness HRC 28-32
HEAT TREATMENT DATA
Soft Annealing : 760 – 780 oC, cooling in furnace, max hardness HB230
Hardening : 1020-1050 oC, in oil or hot bath 500-550 oC
Hardness : after quenching HRC 49
TEMPERING
| Temperature (‘C) | 100 | 200 | 300 | 400 | 500 | 600 |
| HRC | 49 | 47 | 46 | 46 | 47 | 32 |
Application
2316 is a stainless steel and tool steel in the class of Plastic mold Selling condition is harden and temper
Hardness in range of 1000 N/mm2 suitable for plastic mold Especially corrosive resistance and rusty
condition mold such as Amino Plastic, PVC, Thermo plastic
Thanks to wear and corrosive resistance properties, it can also apply to shaft and other parts of water pump
Also, good to use in machinery part that require strength with corrosive resistance. For example,
• High corrosive Plastic mold
• Plastic extrusion mold
• Machinery part , shaft of water pump and staple part
• Compressor part
• Insert sleeve which made of 2083 to enhance strength and corrosive properties.
Filed under: Plastic Mould Steel, Tool Steel | Tagged: 2311 baja impor, 2316 calendar, 2316 catalog pdf, 2316 esr steel, 2316 harga bekas, 2316 material equivalent, 2316 steel adalah, 2316 steel density, 2316 steel equivalent, 2316 steel grade, 2316 steel properties, 2316 vs 2085 steel, aisi p20 properties, alamat stilmetindo prima, ASSAB 2316, assab p20 equivalent, baja edelstahl 2316, baja m300, bohler m303 equivalent, buderus 2316 steel, DIN 1.2316 equivalent materials, din 2316 steel, distributor baja hitachi, harga baja 2316 per kg, harga baja 2316 potongan, harga baja stavax terbaru, harga baja thyssenkrupp 2316, harga steel 2316, importir baja, importir baja perkakas, jual baja 2316 potongan, jual baja thyssen 2316, jual besi 2316 di jakarta, jual material stavax, material 2316 plastic mould steel, material baja stavax, P20 steel, persamaan din 2316, plastic mould steel 2316, ramaxs equivalent, spesifikasi baja 2316, stavax indonesia, stavax steel equivalent, steel m310 bohler, Thyssenkrupp 2316 ESR, Thyssenkrupp 2316 properties, thyssenkrupp indonesia |